ARTIFICIAL JOINTS TRIBOLOGY
https://doi.org/10.51523/2708-6011.2005-2-4-25
Abstract
The article reviews material used for production of movable joints endoprostheses. Statistical data on deterioration of endoprosthetic materials in vivo are presented. The paper emphasizes on the deterioration of superhigh-polymeric polyethylene as of the basic polymer friction material in joints endoprostheses. It has been concluded that mechanisms of implants deterioration greatly differ from the mechanisms of functioning of natural joints. Endoprostheses deterioration in vivo happens in more severe conditions than those at stand tests.
References
1. Ермаков С.Ф., Родненков В.Г., Белоенко Е.Д., Купчинов Б.И. Жидкие кристаллы в технике и медицине. - Мн.-М, 2002. - 412 с.
2. Загородний Н.В., Ильин А.А., Карпов В.Н., Надеждин А.М., Скворцова С.В., Сергеев С.В., Плющев А.А., Гаврюшенко Н.С. Титановые сплавы в эндопротезировании тазобедренного сустава // Вестник травматологии и ортопедии им. Н.Н. Приорова. - 2000. - № 2. - С. 73-75.
3. Кадолич Ж.В. Физическое модифицирование сопряжений полимер-металл для повышения их износостойкости на основе моделирования биофизических свойств естественных суставов. - Дис. … канд. тех. наук. - Гомель, 2002.
4. RM - чашка металл/металл // Margo Anterior. - 2000. - № 4. - С. 5.
5. Фокин В,А. Пары трения для тотальных эндопротезов тазобедренного сустава и проблема износа // Margo Anterior. - 2000. - № 4. - С. 1-4.
6. Blomer W. Design aspects of modular inlay fixation // In: Performance of the wear couple BIOLOX forte in hip arthroplasty. - Proc. 2-nd Symp. on Ceramic Wear Couple, Stuttgart. - Verlag, 1997. - Р. 95-104.
7. Cooper J.R., Dowson D., Fisher J. Macroscopic and microscopic wear mechanisms in ultra-high molecular weight polyethylene // Wear. - 1993. - Vol. 162-164. - Р. 378-384.
8. Hall R.M., Unsworth A., Wroblewski B.M., Burgess I.C. Frictional characterization of explanted Charnley hip prostheses // Wear. - 1994. - Vol. 175. - Р. 159-166.
9. Кnoll J. Analyse von druckverteilung und schmierfilmbildung im kunstlichen huftgelenk // Schmiertechnik und Tribologie. - 1978. - Vol. 25. - № 2. - Р. 43-46.
10. Levitin M. Friction reduction in hip implants treated with regular microrelief // Haifa: Regmi-Tech. - 1997. - 12 p.
11. Mc Kellor H.A., Sarmiento A., Schwinn C.P., Ebramzaden E. In vivo wear of titanium - alloy hip prostheses // J. of Bone and Joint Surgery. - 1990. - Vol. 72. - № 4. - Р. 512-517.
12. Patent 6242507 USA. Process for medical implant cross - linked ultrahigh molecular weight polyethylene having improved balance of wear properties and oxidation resistance / Saum K.A., Sanford W.M., DiMao W.G., Howard E.G. IPC C 08 J 3/28. - 2001.
13. Plitz W., Hoss H.U. Untersuchungen zum verschleibmechanismus bei revidierten huftendoprothesen mit gleitflachen aus Al2O3-keramic // Biomed. Tech. - 1980. - Vol. 25 - P. 165-168.
14. Streicher R.M. Tribologie künstlicher gelenke // In: Endoprothetik / Ed. by E.W. Morscher/ - Berlin-Springer, 1995. - P. 38-53.
15. Zichner L.P., Willert H.G. Comparison of alumina-polyethylene and metal-polyethylene in clinical trials // Clin. Orthop. - 1992. - Vol. 282. - P. 86-94
Review
For citations:
Nikolaev V.I. ARTIFICIAL JOINTS TRIBOLOGY. Health and Ecology Issues. 2005;(4):123-131. (In Russ.) https://doi.org/10.51523/2708-6011.2005-2-4-25
Views: 321
Email this article 